Precipitation behavior of Ag-Pd-In dental alloys

Cited 11 time in webofscience Cited 0 time in scopus
  • Hit : 247
  • Download : 0
Age-hardening characteristics and precipitation behavior of Ag-25%Pd-3%In-1%Zn-0.5%Ir alloy were investigated in detail by means of hardness testing, X-ray diffraction, electron microscopy and resistivity measurement. The solution treating could be accomplished at 980 degrees C and the aging in the temperature range from 950 to 850 degrees C occurred by continuous precipitation. The aging in the temperature range from 850 to 450 degrees C occurred first, forming GP-zones with a hardness increase and then in overaging stage by forming discontinuous precipitation, which consisted of lamellae of solute (Pd, In, Zn) depleted Ag-rich phase and (Pd,Ag)(3)(In,Zn) intermetallic phase. The hardness increased very fast to its peak in 10 min during aging at temperatures between 450 and 550 degrees C. (C) 2000 Kluwer Academic Publishers.
Publisher
KLUWER ACADEMIC PUBL
Issue Date
2000-01
Language
English
Article Type
Article
Citation

JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, v.11, no.1, pp.43 - 48

ISSN
0957-4522
DOI
10.1023/A:1008937702722
URI
http://hdl.handle.net/10203/70600
Appears in Collection
MS-Journal Papers(저널논문)
Files in This Item
There are no files associated with this item.
This item is cited by other documents in WoS
⊙ Detail Information in WoSⓡ Click to see webofscience_button
⊙ Cited 11 items in WoS Click to see citing articles in records_button

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0