Size-Controlled Polymer-Coated Nanoparticles as Efficient Compatibilizers for Polymer Blends

Cited 64 time in webofscience Cited 0 time in scopus
  • Hit : 442
  • Download : 0
Polymer-coated gold nanoparticles (Au NPs) with controlled size and surface chemistry were successfully synthesized and applied to tailor the structures and properties of polytriphenylamine (PTPA) and polystyrene (PS) blends. Two different polymer-coated Au NPs with sizes of 5.9 nm (Au NP-1) and 20.7 nm (Au NP-2) were designed to be thermally stable above 200 degrees C and neutral to both PS and PTPA phases. Hence, both Au NPs localize at the PS/PTPA interface and function as compatibilizers in the PS/PTPA blend. To show the compatibilizing effect of the particles, the morphological behaviors of PS/PTPA blends containing different particle volume fractions (phi(p)) of Au NPs were observed using cross-sectional TEM, and for quantitative analysis, the size distribution of PTPA droplets in the PS matrix was obtained for each sample. The number-average droplet diameter (D(n)) of the PTPA domain in the blend was dramatically reduced from 1.4 mu m to 500 nm at a small phi(p) of 1.0 vol % Au NP-1. The same trend of decreasing D(n) was also observed with the addition of larger Au NP-2, but a higher phi(p) was required to obtain the same amount of reduction in the PTPA droplet size. The phi(p) required to fully cover the PS/PTPA interface as a packed monolayer of Au NPs was calculated as 0.98 vol % for Au NP-1 and 3.38 vol % for Au NP-2, thus giving excellent agreement with critical phi(p) values for the saturation of the PTPA droplet diameter D(n). To demonstrate the effectiveness of Au NPs as compatibilizers, polystyrene-b-poly(triphenylamine) (PS-b-PTPA) block copolymers were also synthesized and used as compatibilizers in the PS/PTPA blend. The decrease in D(n) with the addition of PS-b-PTPA was always smaller than that with addition of Au NP-1 at the same phi(p), indicating that Au NPs are more effective compatibilizers. This different behavior can be attributed to the presence of PS-b-PTPA compatibilizers as micelles or free chains in the homopolymer matrix. In contrast, most Au NPs were strongly adsorbed to the PS/PTPA interface.
Publisher
AMER CHEMICAL SOC
Issue Date
2011-12
Language
English
Article Type
Article
Keywords

BLOCK-COPOLYMER; GOLD NANOPARTICLES; MOLECULAR-WEIGHT; BICONTINUOUS MICROEMULSIONS; EMULSION POLYMERIZATION; SILICA PARTICLES; FACILE SYNTHESIS; SOLAR-CELLS; LOCATION; CHAIN

Citation

MACROMOLECULES, v.44, no.24, pp.9852 - 9862

ISSN
0024-9297
URI
http://hdl.handle.net/10203/100462
Appears in Collection
CBE-Journal Papers(저널논문)
Files in This Item
There are no files associated with this item.
This item is cited by other documents in WoS
⊙ Detail Information in WoSⓡ Click to see webofscience_button
⊙ Cited 64 items in WoS Click to see citing articles in records_button

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0