Estimation of hysteresis loss in Sm1Ba2Cu3O7-delta coated conductor via scanning Hall probe measurements with simultaneously applied field and current

Cited 4 time in webofscience Cited 0 time in scopus
  • Hit : 725
  • Download : 0
The hysteresis loss in a Sm1Ba2Cu3O7-delta coated conductor was estimated from magnetic field profiles measured by the scanning Hall probe method. Current, I-a, and magnetic field, B-a, were applied simultaneously; B-a was applied in the normal direction with respect to the tape surface. B-a and I-a were varied from B-peak to -B-peak and from I-peak to -I-peak, respectively, with the ratio alpha = I-a/B-a fixed during the variation. Three values of a were taken for the three load lines. The values of B-peak/I-peak were varied from 0 mT/0 A to 10.7 mT/116 A, 99.1 mT/50 A, and 298.2 mT/46.1 A, respectively, for the three load lines. From the measured values of magnetic field profiles, the current profiles were calculated by the iterative inversion method. From the current profiles, the flux density profiles and the hysteresis loss, Q, were then calculated for various values of I-peak(=alpha B-peak) in each load line. The results were compared with theoretical calculations based on Brandt's model. When B-peak was about 300 mT, the estimated values of Q were several times smaller than the theoretical values of Q with the self-field I-c0. The low value of Q in this case is due to the field dependent I-c and the saturation effect of the current profiles, which results in significant reduction of the induced magnetic moment, M.
Publisher
IOP PUBLISHING LTD
Issue Date
2009-04
Language
English
Article Type
Article
Keywords

II-SUPERCONDUCTOR STRIP; AC LOSS CHARACTERISTICS; MAGNETIC-FIELD; TRANSPORT CURRENT; FLUX-PENETRATION; SUBSTRATE; COEVAPORATION

Citation

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, v.22

ISSN
0953-2048
DOI
10.1088/0953-2048/22/4/045001
URI
http://hdl.handle.net/10203/99725
Appears in Collection
PH-Journal Papers(저널논문)
Files in This Item
There are no files associated with this item.
This item is cited by other documents in WoS
⊙ Detail Information in WoSⓡ Click to see webofscience_button
⊙ Cited 4 items in WoS Click to see citing articles in records_button

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0