A structural transition of Ba6Ti17O40/BaTiO3 interfaces from faceted to rough was induced by reducing oxygen partial pressure in the atmosphere. As the oxygen partial pressure decreased, the number densities of {111} twins and abnormal grain decreased. TEM observation showed that the twin formation was governed only by the faceting of the interface. Experimental evidence of {111} twin-assisted abnormal growth of faceted BaTiO3 grains was also obtained.