Effect of temperature on fatigue crack growth rate in inconel 690 = 인코넬 690의 피로균열성장속도에 미치는 온도의 영향

Cited 0 time in webofscience Cited 0 time in scopus
  • Hit : 360
  • Download : 0
The effect of temperature on fatigue crack growth rate in Inconel 690 steam geneator tube was invastigaed at room temperature, 150℃, 300℃ and 400℃ in air environment. Fatigue tests was performed on compact tension(CT) specimens made to thichness 8mm. Heat treatment was performed to obtain various microstructures. Tests was conducted at load ratio 0.1, at frequency 10Hz using sinusoidal waveform. Crack length was monitored by compliance method using sensor probe. Tensile tests was performed to obtain yield strength for fatigue test at each testing temperature. Fracture modes were studied using scanning electon microscopy(SEM). Tensile properties of Inconel 690 were dependent on grain size and testing temperature. As temperature and grain size increased, yield strength decreased. At temperature above 300℃, the serrations which were an evidence of dynamic strain aging (DSA) were observed for all cases of materials. Fatigue crack growth rate decreased with increading grain size. At low Δ K, grain size effect was significant at room temperature, which was due to roughness induced crack closure. With increasing temperature, fatigue crack growth rate increased and grain size effect decreased. Chormium carbides which have large size and semi-continuous distribution in the grain boundaries decreased fatigue crack growth rate.
Advisors
Kim, In-SupHwang, Yong-Seok김인섭황용석
Description
한국과학기술원 : 원자력공학과,
Publisher
한국과학기술원
Issue Date
1997
Identifier
114545/325007 / 000953452
Language
eng
Description

학위논문(석사) - 한국과학기술원 : 원자력공학과, 1997.2, [ vii, 46 p. ]

Keywords

Chromium carbide; Nickel base alloy; 인코넬 690; 피로균열성장속도; 크롬탄화물; 니켈기지합금; Inconel 690; Fatigue crack growth rate

URI
http://hdl.handle.net/10203/49372
Link
http://library.kaist.ac.kr/search/detail/view.do?bibCtrlNo=114545&flag=dissertation
Appears in Collection
NE-Theses_Master(석사논문)
Files in This Item
There are no files associated with this item.

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0