Properties of Alkali-Activated Slag Paste Using New Colloidal Nano-Silica Mixing Method

Cited 6 time in webofscience Cited 0 time in scopus
  • Hit : 246
  • Download : 26
Previous studies of alkali-activated slag cement (AASC) using nano-silica have mentioned mostly powdered nano-silica and binder weight replacement methods, which have a rapid decrease in fluidity, a short setting time and a low nano-silica replacement rate (< 5%). In this study, colloidal nano-silica (CNS) was used and the mixing-water weight substitution method was applied. The substitution method was newly applied to improve the dispersibility of nano-silica and to increase the substitution rate. In the experiment, the CNS was replaced by 0, 10, 20, 30, 40, and 50% of the mixing-water weight. As a result, as the substitution rate of CNS increased, the fluidity decreased, and the setting time decreased. High compressive strength values and increased rates were also observed, and the diameter and volume of pores decreased rapidly. In particular, the increase of CNS replacement rate had the greatest effect on decrease of medium capillary pores (50-10 nm) and increase of gel pores (< 10 nm). The new displacement method was able to replace up to 50% of the mixing water. As shown in the experimental results, despite the high substitution rate of 50%, the minimum fluidity of the mixture was secured, and a high-strength and compact matrix could be formed.
Publisher
MDPI
Issue Date
2019-05
Language
English
Article Type
Article
Citation

MATERIALS, v.12, no.9

ISSN
1996-1944
DOI
10.3390/ma12091571
URI
http://hdl.handle.net/10203/262821
Appears in Collection
CE-Journal Papers(저널논문)
Files in This Item
000469757500212.pdf(10.75 MB)Download
This item is cited by other documents in WoS
⊙ Detail Information in WoSⓡ Click to see webofscience_button
⊙ Cited 6 items in WoS Click to see citing articles in records_button

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0