극저온 환경에서 탄소섬유강화 복합재료의 수지조성변화에 따른 인장 물성 측정TENSILE PROPERTIES OF CARBON FIBER COMPOSITES WITH DIFFERENT RESIN COMPOSITIONS AT CRYOGENIC TEMPERATURE

Cited 0 time in webofscience Cited 0 time in scopus
  • Hit : 385
  • Download : 1903
In this study, carbon riber reinforced polymeric (CFRP) composites with differnt rein composition were manufactured and resin formulation in composite materials were presented through tensile tests for cryogenic use. Thermo-methanical cyclic loading( up to 6 ctycles)was applied to CFRP unidirectional laminate specimens from room temperature to -150. Tensile tests were then performed at 0150 using an environmental test chamber. In addition, matrix-dominant properties such as the transverse and in-plene shear characteristics of each omposite model were measured at 0150 to examine the effects of resin formulation on their interfacial properties. The tensile tests showed that the composite models with large amounts of bisphenol-A epoxy and CTBN modified rubber in theri resin composition had good mechanical performance at cryogenic temperature(CT).
본 연구에서는 에폭시 수지조합에 따른 탄소섬유강화 복합재 프리프레그 제작 및 극저온 인장시험을 통해 극저온에서 우수한 기계적 물성을 갖는 복합재 수지조합을 제시하였다. 환경챔버를 이용하여 상온으로부터 -150까지 6회의 열-하중 사이클을 수행한 일방향 복합재 시편에 대하여 -150에서 복합재의 인장강도와 강성을 측정하였다. 또한, -150에서 복합재의 섬유수직방향 인장물성 및 면내 전단물성과 같은 모재 지배적인 물성 측정을 통해 수지조성변화가 섬유와 모재의 계면에 미치는 영향을 고찰하였다. 그 결과, bisphenol-A 형의 에폭시와 CTBN 고무 변성 형 필러를 비교적 다량으로 함유한 수지조성을 갖는 복합재 시편이 극저온에서 우수한 기계적 물성을 보임을 확인하였다.
Publisher
한국복합재료학회
Issue Date
2007-08
Keywords

탄소섬유강화 복합재료; 극저온; 인장시험; 수지조성

Citation

한국복합재료학회지, Vol.20, No.4

ISSN
1598-6934
URI
http://hdl.handle.net/10203/25206
Appears in Collection
AE-Journal Papers(저널논문)
Files in This Item
1-138.pdf(554.36 kB)Download

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0