(The) effect of iron addition on the microstructures and mechanical properties of Cu-11.0% Al alloyCu-11.0% Al합금에의 철 첨가가 현미 경조직과 기계적 성질에 미치는 영향

Cited 0 time in webofscience Cited 0 time in scopus
  • Hit : 391
  • Download : 0
The effect of iron addition to Cu-11.0\% Al alloy on the mechanical properties and microstructures has been investigated by using isothermal transformation technique. This investigation showed that the addition of 2\% iron to Cu-11.0\% Al alloy produced fine microstuctures and that fine ironrich precipitate particles were formed within $\alpha$ phase after proper isothermal treatments. However, the addition of 1\% iron did not have any effect on the microstructures at transformation temperature of 524$^\circ$C and 560$^\circ$C. The structure of iron-rich precipitate particles was body centered cubic (B.C.C.) with lattice parameter of 2.93A. The iron additions caused increase in ultimate tensile strength (U.T.S.) and 0.2\% offset yield strength with little effect on elongation. The specimens of fine microstructures with ironrich precipitate particles showed large U.T.S., and the maximum value of 110,000 psi was obtained. The high U.T.S. is attributed to the microstructural refinement and the iron-rich precipitate particles.
Advisors
Chun, Soung-Soonresearcher천성순researcher
Description
한국과학기술원 : 재료공학과,
Publisher
한국과학기술원
Issue Date
1976
Identifier
62082/325007 / 000731048
Language
eng
Description

학위논문(석사) - 한국과학기술원 : 재료공학과, 1976, [ iii, 43 p. ]

URI
http://hdl.handle.net/10203/51449
Link
http://library.kaist.ac.kr/search/detail/view.do?bibCtrlNo=62082&flag=dissertation
Appears in Collection
MS-Theses_Master(석사논문)
Files in This Item
There are no files associated with this item.

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0