Study on the deposition of $YBa_2Cu_3O_{7-δ}}$ bi-crystalline thin films using the $BaF_2$ -process and their properties = $BaF_2$-process를 이용한 $YBa_2Cu_3O_{7-δ}}$ bi-crystalline 박막의 증착 및 특성에 관한 연구

Cited 0 time in webofscience Cited 0 time in scopus
  • Hit : 580
  • Download : 0
DC FieldValueLanguage
dc.contributor.advisorYoum, Do-Jun-
dc.contributor.advisor염도준-
dc.contributor.authorKim, Jong-Yun-
dc.contributor.author김종윤-
dc.date.accessioned2011-12-14T07:57:18Z-
dc.date.available2011-12-14T07:57:18Z-
dc.date.issued2003-
dc.identifier.urihttp://library.kaist.ac.kr/search/detail/view.do?bibCtrlNo=179975&flag=dissertation-
dc.identifier.urihttp://hdl.handle.net/10203/48624-
dc.description학위논문(석사) - 한국과학기술원 : 물리학과, 2003.2, [ [ii], 70 p. ]-
dc.description.abstract$YBa_2Cu_3O_{7-δ}(YBCO)$ thin films were formed using the $BaF_2$-process. This process comprises two steps. First, a precursor film which is a fine mixture of $BaF_2$ and metallic Y and Cu was deposited using thermal co-evaporation. Then it was heated in a flowing atmosphere containing $N_2$ and $O_2$ gases and water vapor to obtain crystallized YBCO films. To find optimal annealing conditions, eight $SrTiO_3(STO)$ single crystals were used as substrates. As a result, annealing temperature of about 720℃, oxygen partial pressure of 100ppm, and water temperature of 50℃ were found to be the most appropriate annealing conditions. Using these conditions, YBCO bi-crystalline thin films were formed on 30℃ and 40℃ [001]-tilt STO bi-crystals. The pole figures and the X-ray diffraction(XRD) data showed good epitaxial growth of the bi-crystalline samples, but their Scanning electron microscope(SEM) images not so good. The critical current densities were 263 and 51MA/㎠ at 77K and zero field for 30℃ and 45℃ bicrystalline samples, respectively. These poor characteristics may be partially due to the considerable amount of fluoride remaining in the annealed films. Resistive transitions at various magnetic fields were measured and the critical temperatures were found to be 89.5K and 88.5K for 30℃ and 45℃ bi-crystalline samples, respectively. Next, it was attempted the preparation of precursor films using ``$YF_3+BaF_2$`` bulk as one of the two evaporation sources. From this, YBCO superconducting thin films were also obtained, the properties of which were comparable to those of $BaF_2$-processed samples. It was also attempted to use Ba metal instead of $BaF_2$, and $YF_3$ instead of Y metal in this process and obtained similar results. Though the use of CuF was not attempted, similar results are likely to be shown. Furthermore, the preparation of precursor film using one-source by thermal co-evaporation or $CO_2$ laser evaporation is expected to be come true someday.eng
dc.languageeng-
dc.publisher한국과학기술원-
dc.subject전구체-
dc.subject바이크리스탈-
dc.subject이트륨바륨카파옥사이드-
dc.subject고온초전도체-
dc.subjectprecursor-
dc.subjectbi-crystal-
dc.subjectYBCO-
dc.subject$\mathrm{BaF_2}$-process-
dc.subjecthigh-temperature superconductor-
dc.subject바륨플로라이드 프로세스-
dc.titleStudy on the deposition of $YBa_2Cu_3O_{7-δ}}$ bi-crystalline thin films using the $BaF_2$ -process and their properties = $BaF_2$-process를 이용한 $YBa_2Cu_3O_{7-δ}}$ bi-crystalline 박막의 증착 및 특성에 관한 연구-
dc.typeThesis(Master)-
dc.identifier.CNRN179975/325007-
dc.description.department한국과학기술원 : 물리학과, -
dc.identifier.uid020013138-
dc.contributor.localauthorKim, Jong-Yun-
dc.contributor.localauthor김종윤-
Appears in Collection
PH-Theses_Master(석사논문)
Files in This Item
There are no files associated with this item.

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0