Study on the fabrication and the characteristics of $Sm_1Ba_2Cu_3O_{7-δ}$ high Tc superconducting films = $Sm_1Ba_2Cu_3O_{7-δ}$ 고온초전도박막 제작과 특성에 관한 연구

Cited 0 time in webofscience Cited 0 time in scopus
  • Hit : 155
  • Download : 0
The growth properties and field dependent critical current densities of $Sm_{1+x}Ba{2-x}Cu_3O{7-\delta}$(SBCO) films on biaxially textured Ni tapes with $CeO_2/YSZ/CeO_2$ buffer layers were investigated.The window of substrate temperature($T_s$) for c-axis normal growth in 5mTorr of oxygen pressure were wider than $150^\circ C$. The upper limit of $T_s$-window was much higher than that of $Y_1Ba_2Cu_3O_{7-\delta}$(YBCO) films. Around the low limit of $T_s$, SBCO films grew in [103] normal textures. The zero field critical currents ($J_c$) were slightly smaller than those of YBCO films, while in high field regions critical current densities are much higher and the estimated pinning energies were less dependent on external fields than that of YBCO. We observed that a $Sm_1Ba_2Cu_3O_{7-\delta}(SBCO) film grown on a YSZ substrate with arbitrarily oriented crystal was textured in a single crystalline orientation, while there seems to be no noticeable relation between the crystalline orientations of the film and the substrate. The SBCO[103] axis was close to the surface normal axis. On the other hand, we could not grow an YBCO film on the same substrate, which implies the growth of SBCO film is more stable than YBCO film on that substrate. The qualities of SBCO films grown at substrate temperatures across a wide range of $680^\circ C$ ~ $750^\circ C$ were similar. The critical current density of this SBCO film was smaller than that of SBCO film on a RABiTS-Ni tape, which is several times smaller than that of the YBCO film of coated conductor. The transport properties of $Sm_1BA_2Cu_3O_{7-\delta}$ films, which were grown on the bi-crystalline $SrTiO_3$ substrates of $24^\circ$, $30^\circ$, $36.8^\circ$ and $45^\circ$ misorientation angles, were investigated by the measurements of the Ⅰ-Ⅴ curves at 77K under various magnetic fields. When the voltages were high enough, the Ⅰ-Ⅴ curves became straight. The resistances estimated from the slopes were almost independ...
Advisors
Youm, Do-Junresearcher염도준researcher
Description
한국과학기술원 : 물리학과,
Publisher
한국과학기술원
Issue Date
2004
Identifier
237497/325007  / 000985340
Language
eng
Description

학위논문(박사)- 한국과학기술원 : 물리학과, 2004.2, [ v, 63 p. ]

Keywords

SUPERCONDUCTING FILMS; SBCO; CRITICAL CURRENT DENSITY; 히스테리시스; 임계전류밀도; 고온초전도박막; HYSTERESIS

URI
http://hdl.handle.net/10203/47334
Link
http://library.kaist.ac.kr/search/detail/view.do?bibCtrlNo=237497&flag=dissertation
Appears in Collection
PH-Theses_Ph.D.(박사논문)
Files in This Item
There are no files associated with this item.

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0