Synthesis of nanomorphic zeolites by sodium-surfactant cooperative structure direction and their catalytic applications = 소듐 이온과 계면활성제의 협력적 구조유도 작용을 이용한 나노형상 제올라이트의 합성 및 촉매 응용에 관한 연구

Cited 0 time in webofscience Cited 0 time in scopus
  • Hit : 113
  • Download : 0
The work presented in this thesis addresses the synthesis of nanomorphic zeolites with controlled thickness and their catalytic application. Zeolites are a family of crystalline aluminosilicates exhibiting ordered micropores. Due to their micropores at the molecular scale and their acidity, they have been widely used in catalysis and separation. Conventional zeolites synthesized with the use of small organic ammonium ions or alkali metals as structure-directing agents (SDAs) typically have micrometer-sized crystals. The limited diffusion of molecules in the crystals often induces an overload on the crystal surface and fast deactivation. To solve this problem, decreasing the diffusion length has been intensively investigated by the synthesis of zeolite as nanomorphic structures. Among the large number of approaches tried, use of an organic surfactant that is functionalized with a zeolite structure-directing group as SDA is one of the most promising strategies. In this thesis, MFI zeolites were synthesized using a small amount of $C_{18} H_{37}-N^{+}(CH^3)_{2} -C_{6}H_{12} -N^{+} (CH_{3})_{2}-C_{6}H_{13}(Br^{-})_{2}$ surfactant $(C_{18-6-6})$ in the absence and presence of $Na^{+}$. In the presence of $Na^{+}$, 2.5 nm thick MFI nanosheets were generated followed by the progressive growth of the nanosheets with the consumption of amorphous aluminosilicate. Under $Na^{+}$-free conditions, the product consisted of 2.5 nm thick nanosheet and amorphous product. It was clearly elucidated that C18-6-6 acted as a SDA for the 2.5 nm zeolite nanosheets, and $Na^{+}$ was involved in the structure direction of the MFI to grow the nanosheets. The structure direction of $C_{18-6-6}$ and $Na^{+}$ was systematically balanced to control the thickness of the MFI zeolites in the range of 2.5 to 20 nm. In addition, the properties of the zeolites were characterized and compared in the conversion of methanol to hydrocarbons. Thicker crystals exhibited higher hydrocarbon yields and shorter lifetimes. These results are explained by the hydrocarbon-pool mechanism and the diffusion in crystals.
Advisors
Ryoo, Ryongresearcher유룡researcher
Description
한국과학기술원 :생명화학공학과,
Publisher
한국과학기술원
Issue Date
2017
Identifier
325007
Language
eng
Description

학위논문(박사) - 한국과학기술원 : 생명화학공학과, 2017.8,[viii, 112 p. :]

Keywords

nanomorphic zeolite▼aMFI zeolite▼astructure directing agent▼athickness of zeolite crystal▼amethanol to hydrocarbons; 나노형상 제올라이트▼aMFI 제올라이트▼a구조 유도체▼a제올라이트의 두께▼a메탄올 탄화수소화 반응

URI
http://hdl.handle.net/10203/241893
Link
http://library.kaist.ac.kr/search/detail/view.do?bibCtrlNo=718844&flag=dissertation
Appears in Collection
CBE-Theses_Ph.D.(박사논문)
Files in This Item
There are no files associated with this item.

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0