High temperature deformation of Ti-(46-48)A1-2W intermetallic compounds

The high temperature deformation behavior of Ti-46Al-2W and Ti-48A1-2W intermetallic compounds have been investigated in isothermal compressive tests, performed at temperatures between 1000 degrees C and 1200 degrees C for strain rates between 10(-3) and 10(-1) s(-1). The stress-strain curve during high temperature deformation exhibits a peak stress which is followed by a gradual decrease into a steady state stress with increasing the strain. The flow softening behavior after the peak stress is attributed to the effects of dynamic recrystallization during deformation. The dependence of flow stress on temperature and strain rate followed a hyperbolic sine relationship using the Zener-Hollomon parameter. The activation energies, Q, were measured as 449 kJ mol(-1) and 394 kJ mol(-1), and the stress exponents were measured as 3.6 and 3.7 for Ti-46Al-2W and Ti-48A1-2W, respectively. The activation energy increased with decreasing Al content in TiAl-base intermetallic compounds. The coefficient between peak stress and Zener-Hollomon parameter, A, was not a constant, but was dependent on the activation energy. The peak stresses can be predicted well by using a normalized Zener-Hollomon parameter. The dynamic recrystallization rate and recrystallized grain size increased with increasing the temperature and with decreasing the strain rate. (C) 1998 Elsevier Science S.A. All rights reserved.
Publisher
ELSEVIER SCIENCE SA
Issue Date
1998-08
Language
ENG
Keywords

GAMMA-TITANIUM ALUMINIDES; MECHANICAL-PROPERTIES; DYNAMIC RECRYSTALLIZATION; ELEVATED-TEMPERATURES; HOT-WORKING; ALLOY; MICROSTRUCTURE; EVOLUTION; FRACTURE

Citation

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, v.251, no.1-2, pp.216 - 225

ISSN
0921-5093
URI
http://hdl.handle.net/10203/2394
Appears in Collection
MS-Journal Papers(저널논문)
  • Hit : 516
  • Download : 14
  • Cited 0 times in thomson ci
This item is cited by other documents in WoS
⊙ Detail Information in WoSⓡClick to seewebofscience_button
⊙ Cited 41 items in WoSClick to see citing articles inrecords_button

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0