Vacuum Hot Pressing 조건이 SiCw/2124AI 금속복합재료의 기계적 성질 및 미세구조에 미치는 영향 Effects of Vacuum Hot Pressing Conditions on Mechanical Properties and Microstructures of SiCw/2124Al Metal Matrix Composites

The variation of the microstructures and the mechanical properties with varying vacuum hot pressing temperature and pressure was investigated in PyM processed 20 vol%) SiCw/ 2124Al composites. As increasing the vacuum hot pressing temperature, the aspect ratio of whiskers and density of composites increased due to the softening of 2124Al matrix with the increased amount of liquid phase. The tensile strength of composite increased with increasing vacuum hot pressing temperature up to $570^{\circ}C$ 수식 이미지 and became saturated above $570^{\circ}C$ 수식 이미지, To attain the high densification of composites above 99%, the vacuum hot pressing pressure was needed to be above 70 MPa. However, the higher vacuum hot pressing pressure above 70 MPa was not effective to increase the tensile strength due to the reduced aspect ratio of SiC whiskers from damage of whiskers during vacuum hot pressing. A phenomenological equation to predict the tensile strength of $SiC_w$ 수식 이미지/2124AI composite was proposed as a function including two microstructural parameters, i.e. density of composites and aspect ratio of whiskers. The tensile strength of $SiC_w$ 수식 이미지/2124AI were found more sensitive to the porosity than other P/M materials due to the higher stress concentration and reduced load transfer efficiency by the pores locating at whisker/matrix interfaces.
Issue Date

한국분말야금학회지, v.1, no.2, pp.159 - 166

Appears in Collection
MS-Journal Papers(저널논문)
Files in This Item
There are no files associated with this item.
  • Hit : 53
  • Download : 0
  • Cited 0 times in thomson ci


  • mendeley


rss_1.0 rss_2.0 atom_1.0